HomeAdvanced high strength cold rolled sheet steels (AHSS) with optimised profiling properties produced through different lines (AHSS-PROFILE)
Final report
Metadati delle pubblicazioni
The current work aimed to develop cold rolled steel sheets with Rm > 1000 MPa optimised for roll forming to be produced in existing continuous annealing lines with either gas (CAL-GQ) or water quenching (CAL-WQ) and in hot dip galvanising (HDG) lines. The result of the project is a significant improvement in roll formability for materials produced in all three lines, compared to state of the art materials of the same strength level. The three steels developed within the project also reached the target values in terms of bendability (Ri/t < 2) and hole expansion ratio (punched) >25%. For the HDG line, the optimum microstructure consisted of bainite and small amounts of untempered martensite to reach the necessary strength level. A key to produce these steels is to avoid polygonal ferrite by using a relative high annealing temperature and well balanced amount of hardenable elements. For CAL-GQ with overaging section, the optimum microstructure consists of lower bainite, tempered martensite, and possibly a few percent ferrite. The process window in this line is largest, even Rm > 1200 MPa materials were produced in this line with good formability. For CAL-WQ with tempering section, the optimum microstructure is a highfraction martensite DP steel tempered at relative high temperature. This steel can be produced with very lean chemistries but controlling the amount and distribution of martensite is challenging.
- Pubblicato:
- Servizio autore: Directorate-General for Research and Innovation (Commissione europea)
- Temi: Metallurgia, siderurgia , Ricerca e sviluppo industriali
- Argomento: iron and steel industry , materials technology , research project , research report , resistance of materials , special steels , steel , technology assessment
|
PDF
|
|||
| ISSN 1831-9424 | ISBN 978-92-79-54039-4 | DOI 10.2777/622704 | Numero di catalogo KI-NA-27615-EN-N |
|
Carta
|
|||
| ISSN 1018-5593 | ISBN 978-92-79-54038-7 | DOI 10.2777/844354 | Numero di catalogo KI-NA-27615-EN-C |
- Released on EU publications website:
Questa pubblicazione può essere scaricata in formato web (PDF) e in formato ottimizzato per la stampa (PDF/X). Per maggiori informazioni su come stampare una propria copia delle pubblicazioni dell'UE, si rimanda alla nostra sezione FAQ.
Visualizzatore di documenti
Note:
La pubblicazione non può essere visualizzata nel visualizzatore di documenti. Apri la versione web
È possibile accedervi da: Download e lingue